SiO2 PRAI 12,5KG 40% FS witbakkend 1100°-1260°

Artikelnr: SiO PRAI
16,00
Verzendmethode
Afhalen MECHELEN:
0,00
Beschrijving

12.5 kg, witbakkend

White stoneware clay body with 40% impalpable grog (0-0.2mm). Formulated for artistic ceramics, it is ideal for wheel-throwing and modeling smooth pieces with fine details. The high content of grog confers an excellent behavior during drying and firing. Its particular ivory color after firing is much appreciated and provides an excellent ware for glazes and coloring oxides, which develop bright and intense tones.

Firing range: Cone 6-10 (2269º-2381ºF)
Biscuit: Cone 06 (1855ºF)
Water content: 19%
Plasticity (IP Atterberg): 16
Carbonate content (CaCO3): 0%
Drying shrinkage: 5.9%
Firing shrinkage at Cone 10: 7.0%
Porosity (water absorption) at Cone 10: 0.0%
Dry bending strength: 3.0 N/mm2
Fired bending strength at Cone 10: 45.3 N/mm2
Thermal coefficient (a25-500ºC): 52.6x10-7ºC-1

Aanbevolen artikelen:

FUCHS
11,00
Steengrijs. 20% chamotte van 0-0.5mm 1000-1250°C
WITGERT
7,50
10 kg witbakkende klei 1000 - 1300°C zonder chamotte
SiO2
14,00
12.5 kg zwartbakkende klei 1000-1260°C Black sculpture clay body with 40% fine grog (0-0.5mm). Formulated for artistic ceramics, it is ideal...
WITGERT
9,00
Antracietbakkende klei max. 1300 °C 25% chamotte 0-0.2mm
FUCHS
8,00
10 kg witbakkende klei 1000-1280°C 40% chamotte van 0-0.5 mm

Alternatieve artikelen:

WITGERT
7,50
10 kg witbakkende klei 1000 - 1300°C zonder chamotte
WITGERT
8,50
Antracietbakkende klei max. 1300°C 0% chamotte
EARTHSTONE
18,50
1120- 1300°C Prachtige Engelse "crank"-klei. Open textuur, grove chamotte, maar toch een enorme plasticiteit. Alle kwaliteiten die...
SiO2
14,00
12.5 kg zwartbakkende klei 1000-1260°C Black sculpture clay body with 40% fine grog (0-0.5mm). Formulated for artistic ceramics, it is ideal...
FUCHS
11,00
Steengrijs. 20% chamotte van 0-0.5mm 1000-1250°C